Glaze type · Traditions & specialties
Carbon-trap shino
Across 56 published recipes: mostly cone 10 and cone 9, fired in reduction and wood; Semi-glossy, opaque.
Materials that define it
Share of recipes containing each material, and the typical amount when present. Materials link to their reference pages.
| Material | In recipes | Typical | Half of recipes |
|---|---|---|---|
| Soda ash | 98% | 8.5% | 4–16.3% |
| Nepheline syenite | 93% | 40.95% | 38.15–45% |
| Ball clay | 80% | 13.8% | 11.75–16.74% |
| EPK | 70% | 9.71% | 5–17% |
| Spodumene | 57% | 15.2% | 14.71–28% |
| Kona F-4 feldspar | 41% | 14.58% | 9.8–18.9% |
| Redart | 27% | 5.72% | 5.66–6% |
| Minspar 200 | 25% | 11% | 10–22.29% |
| Bentonite | 18% | 1.97% | 1–2% |
| Kaolin | 14% | 11% | 9.77–17.9% |
| Custer feldspar | 7.1% | 37.82% | 10.5–66.55% |
| Soda feldspar | 7.1% | 10.05% | 9.3–13.95% |
| Potash feldspar | 3.6% | 27.58% | 15.16–40% |
| Yellow iron oxide | 3.6% | 1.5% | 0.5–2.5% |
Typical fired chemistry
Median oxide analysis (weight %) across the recipes that report one, with the interquartile range. Silica and alumina set the melt; the fluxes and colorants make the family.
| Oxide | Median | Half of recipes |
|---|---|---|
| SiO2 | 56.45% | 48.56–58.77% |
| Al2O3 | 22.07% | 21.4–23.16% |
| Na2O | 8.37% | 7.44–12.66% |
| K2O | 2.66% | 2.36–3.07% |
| Li2O | 1.22% | 1.18–2.24% |
| CaO | 0.53% | 0.42–0.67% |
| Fe2O3 | 0.32% | 0.23–0.72% |
Related types
Questions
- What is a Carbon-trap shino glaze?
- In 56 published recipes, Carbon-trap shino glazes are mostly fired to cone 10 and cone 9 in reduction and wood, with a Semi-glossy, opaque result. The defining materials are Soda ash, Nepheline syenite, Ball clay, EPK, Spodumene.
- What cone is Carbon-trap shino fired to?
- The most common cones in published recipes are cone 10 and cone 9; the full distribution is on this page. Atmosphere matters as much as cone for this family: reduction and wood.
- What is the typical chemistry of a Carbon-trap shino glaze?
- Median fired analysis: SiO2 56.45%, Al2O3 22.07%, Na2O 8.37%, K2O 2.66%, Li2O 1.22%, CaO 0.53%. Treat these as the centre of a range, not a target — the same family spans different fluxes and cones.
Sources. Every figure is a statistic computed by Claybench over 10,859 glaze recipes compiled from publicly shared community recipe collections (snapshot 2026-02-27); no recipe is reproduced. Colour-chemistry notes are paraphrased from Linda Arbuckle's Ceramic Materials handout.
Colorant and flux notes touch on materials with handling hazards (barium, cobalt, chrome, manganese, lead in historic recipes). Read each material's page and its supplier SDS before mixing; test any food surface.